Ignition of a thermite reaction normally requires supervision by a trained technician, and may require persistent efforts, as ignition can be unreliable and unpredictable. Thermite reactions require very high temperatures for initiation. These temperatures cannot be reached with conventional black powder fuses, nitrocellulose rods, detonators, a suitable pyrotechnic initiator, or other common igniting substances. Even when the thermite is hot enough to glow bright red, it will not ignite as it must be at or near white-hot to initiate the reaction. It is possible to start the reaction using a propane torch if done correctly. The torch can preheat the entire pile of thermite which will make it explode instead of burning slowly when it finally reaches ignition temperature.

Often, strips of magnesium metal are used as fuses. Because metals burn without releasing cooling gases, they can potentially burn at extremely high temperatures. Reactive metals such as magnesium can easily reach temperatures sufficiently high for thermite ignition. However, this method is notoriously unreliable: Magnesium itself is difficult to ignite, and in windy or wet conditions the strip may be extinguished. Also, magnesium strips do not contain their own source of oxygen so combustion cannot occur unless the magnesium strips are exposed to air. A significant danger of magnesium ignition is the fact that the metal is an excellent conductor of heat; heating one end of the ribbon may cause the other end to transfer enough heat to the thermite to cause premature ignition. Despite these issues, magnesium ignition remains popular amongst amateur thermite users, mainly because it can be easily obtained.

The reaction between potassium permanganate and glycerine or ethylene glycol is used as an alternative to the magnesium method. When these two substances mix, a spontaneous reaction will begin, slowly increasing the temperature of the mixture until flames are produced. The heat released by the oxidation of glycerine is sufficient to initiate a thermite reaction. However, this method can also be unreliable and the delay between mixing and ignition can vary greatly due to factors such as particle size and ambient temperature.

Apart from magnesium ignition, some amateurs also choose to use sparklers to ignite the thermite mixture. These reach the necessary temperatures and provide enough time before the burning point reaches the sample. However, this can be a dangerous method, as the iron sparks, like the magnesium strips, burn at thousands of degrees and can ignite the thermite even though the sparkler itself is not in contact with it. This is especially dangerous with finely powdered thermite.

Similarly, finely-powdered thermite can be ignited by a regular flint spark lighter, as the sparks are burning metal (in this case, the highly-reactive rare-earth metals lanthanum and cerium). Therefore it is unsafe to strike a lighter close to thermite.

A stoichiometric mixture of finely powdered iron(III) oxide and aluminium may be ignited using ordinary red-tipped book matches by partially embedding one match head in the mixture, and igniting that match head with another match, preferably held with tongs in gloves to prevent flash burns.

Laser beam welding is a welding process which produces coalescence of materials with the heat obtained from the application of a concentrated coherent light beam impinging upon the surfaces to be joined.

The focused laser beam has the highest energy concentration of any known source of energy. The laser beam is a source of electromagnetic energy or light that can be projected without diverging and can be concentrated to a precise spot. The beam is coherent and of a single frequency.

Producing a laser beam is extremely complex. The early laser utilized a solid-state transparent single crystal of ruby made into a rod approximately an inch in diameter and several inches long. The end surfaces of the ruby rod were ground flat and parallel and were polished to extreme smoothness.

The laser can be compared to solar light beam for welding. The laser can be used in air. The laser beam can be focused and directed by special optical lenses and mirrors. The laser can operate at considerable distance from the work piece.

When using the laser beam for welding the electromagnetic radiation impinges on the surface of the base metal with such a concentration of energy that the temperature of the surface is melted and volatilized. The beam penetrates through the metal vapor and melts the metal below. One of the original questions concerning the use of the laser was the possibility of reflectivity of the metal so that the beam would be reflected rather than heat the base metal. It was found, however, that once the metal is raised to its melting temperature the surface conditions have little or no effect.

The welding characteristics of the laser and of the electron beam are similar. The concentration of energy by both beams is similar, with the laser having a power density in the order of 106 watts per square centimeter. The power density of the electron beam is only slightly greater. This is compared to a current density of only 104 watts per square centimeter for arc welding.

Laser beam welding has a tremendous temperature differential between the molten metal and the base metal immediately adjacent to the weld. Heating and cooling rates are much higher in laser beam welding than in arc welding, and the heat-affected zones are much smaller. Rapid cooling rates can create problems such as cracking in high carbon steels.

The laser beam has been used to weld carbon steels, high strength low alloy steels, aluminum, stainless steel and titanium. Laser welds made in these materials are similar in quality to welds made in the same materials by electron beam process.

Thermite welding is the process of igniting a mix of high energy materials, also called thermite, that produce a metallic slag that is poured between the working pieces of metal to form a joint. It was developed by Hans Goldschmidt around 1895.

Commonly utilizing the composition of 5 parts iron oxide red (rust) powder and 3 parts aluminium powder ignited at high temperatures. A violent reaction occurs that produces through reduction and oxidation a white hot iron slag and vaporous aluminium oxide. This form of welding is still widely used to weld railway rails. This form of welding is also in use today for example for quick fixes on ship hull punctures and the likes. Weld quality is low due to the fact of low to nil carbon content in the filling metal and low heat penetration into the joining metals. This method is usually used in conjunction with oxyacetylene flame to create a good fusion with the working pieces of metal.

From Wikipedia, the free encyclopedia